$************************RELEASE VERSION*********************************** $ $ mc_mg_v2.01.tdb $ $************************RELEASE VERSION*********************************** $ $ MatCalc thermodynamic database for magnesium alloys. $ $ Created 2016-01-13 $ Release 14.9.2023 by MatCalc Engineering GmbH. $ $ This database contains edited and newly assessed thermodynamic data $ for Mg-base alloys. $ Thermodynamic parameters have been assessed at TU Wien $ by Povoden-Karadeniz Erwin. $ $ ######################################################################### $ $ use with MatCalc version 6.00 or higher. $ $ ######################################################################### $ $ Copyright and editor: Erwin Povoden-Karadeniz $ (erwin.povoden-karadeniz@tuwien.ac.at) $ $ This database mc_mg_v2.01.tdb is made available under the $ Open Database License: http://opendatacommons.org/licenses/odbl/1.0/. $ Any rights in individual contents of the database are licensed under the $ Database Contents License: http://opendatacommons.org/licenses/dbcl/1.0/. $ $ ########################################################################## $ The following assessments are incorporated in this database: $ $ ... see list of publications in the reference section $ at the end of this file ... $ The following elements are included in this database: $ $ Mg, Al, Ca, Mn, Si, Sr, Zn $ Ambit $ This database version has been designed and tested to be used $ for thermokinetic simulations in AZ Mg-alloys $ from melting to room temperature. $ For kinetic simulations at low temperature, the low temperature limits $ of Gibbs energies were reduced from 298.15 K, as given by Ref 0, to 273.00 K. $ For kinetic simulations at very high temperatures, the high temperature limits $ of Gibbs energies were in some cases extended to higher temperatures $ than given by Ref 0. $ Ternary Al-Ca-Mn, Al-Ca-Si, Al-Ca-Sr, Al-Ca-Zn, Al-Mg-Sr, Al-Mn-Sr, $ Al-Si-X (except Al-Si-Mg), Al-Sr-X, Mg-Mn-Zn, Mg-Mn-Si, Mg-Si-Sr, Mn-Si-X, $ Mn-Sr-Zn, Si-Sr-Zn, and higher orders are ideal extension from the binaries. $ Thermodynamic equilibrium calculations have been tested for wrought alloys $ with x(Mg) > 0.95. $ The following phases are included in this database: $ $ The following phases are included in this database: $ They are listed in the order of their appearance in $ part D) Thermodynamic model parameters for phases. $ For their documentation see part D). $ Documentation and priority rankings suggested by the editor are visible $ in the MatCalc databases window after reading the database $ and marking the phase of interest. $ $ LIQUID $ $ Alloy phases $ HCP_A3 HCP_ZN BCC_A2 FCC_A1 ALPHA_MN BETA_MN $ intermetallic equilibrium phases listed in the same order $ as in section IV by relevance in Mg-alloys. $ ALMG_BETA ALMG_EPS G_AL12MG17 ALMGMN_T AL4MN AL6MN AL8MN5_D810 $ AL11MN4 AL12MN AL3X8 AL4X AL14CA13 AL2SR AL7SR8 C2M5Z13 C2M6Z3 $ CAZN CAZN2 CAZN3 CAZN5 CAZN11 CAZN13 CA3ZN CA5ZN3 $ IM1 IM2 IM3 IM4 LAV_C14 LAV_C15 LAV_C36 MG2SI MG17X2 MG23X6 $ MG38SR9 MGZN MG2ZN11 MG2ZN3 MG7ZN3 MN3SI PHI $ SI_DIAMOND_A4 SRZN SRZN5_LT TAU $************************************************************************** $ $ A) Definition of elements $ From A. T. Dinsdale, SGTE data for pure elements (Ref 0) $ $************************************************************************** $ $Element Standard state mass [g/mol] enthalpy_298 entropy_298 ELEMENT VA VACUUM 0.00 0.00 0.00 ! ELEMENT AL FCC_A1 26.98154 4540.00 28.30 ! ELEMENT CA FCC_A1 40.078 5736.00 41.588 ! ELEMENT MG HCP_A3 24.305 4998.00 32.671 ! ELEMENT MN BCC_A12 54.938 4995.696 32.2206 ! ELEMENT SI DIA_A4 28.0855 3217.00 18.81 ! ELEMENT SR FCC_A1 87.62 6568.00 55.694 ! ELEMENT ZN HCP_A3 65.38 5656.70 41.631 ! $************************************************************************** $ $ B) MatCalc specific commands $ $************************************************************************** $ $ Defines MG as reference element REFERENCE_ELEMENT MG ! $ $************************************************************************** $ enthalpy of vacancy formation $************************************************************************** $ $ default for hcp_A3 is MG PARAMETER HMVA(HCP_A3,*;0) 273.00 +86836.78; 6000.00 N REF:pov11 ! $ PARAMETER HMVA(HCP_A3,AL:*;0) 273.00 +70000; 6000.00 N REF:pov15 ! PARAMETER HMVA(HCP_A3,CA:*;0) 273.00 +70000; 6000.00 N REF:pov15 ! PARAMETER HMVA(HCP_A3,MG:*;0) 273.00 +70000; 6000.00 N REF:pov15 ! PARAMETER HMVA(HCP_A3,MN:*;0) 273.00 +70000; 6000.00 N REF:pov15 ! PARAMETER HMVA(HCP_A3,SI:*;0) 273.00 +70000; 6000.00 N REF:pov15 ! PARAMETER HMVA(HCP_A3,SR:*;0) 273.00 +70000; 6000.00 N REF:pov15 ! PARAMETER HMVA(HCP_A3,ZN:*;0) 273.00 +70000; 6000.00 N REF:pov15 ! $ $************************************************************************** $ $ C) Gibbs energy functions of elements, SER (Standard elements references) $ $************************************************************************** $ FUNCTION GHSERAL 273.00 -7976.15+137.093038*T-24.3671976*T*LN(T) -0.001884662*T**2-8.77664E-07*T**3+74092*T**(-1); 700.00 Y -11276.24+223.048446*T-38.5844296*T*LN(T)+0.018531982*T**2 -5.764227E-06*T**3+74092*T**(-1); 933.47 Y -11278.378+188.684153*T-31.748192*T*LN(T)-1.230524E+28*T**(-9); 6000.00 N REF:2 ! FUNCTION GHSERCA 273.00 -4955.062+72.794266*T-16.3138*T*LN(T) -0.01110455*T**2-133574*T**(-1); 1115.00 Y -107304.428+799.982066*T-114.292247*T*LN(T)+0.023733814*T**2 -1.2438E-06*T**3+18245540*T**(-1); 6000.00 N REF:2 ! FUNCTION GHSERMG 273.00 -8367.34+143.675547*T-26.1849782*T*LN(T) +4.858E-04*T**2-1.393669E-06*T**3+78950*T**(-1); 923.00 Y -14130.185+204.716215*T-34.3088*T*LN(T)+1.038192E+28*T**(-9); 6000.00 N REF:2 ! FUNCTION GHSERMN 273.00 -8115.28+130.059*T-23.4582*T*LN(T) -7.34768E-3*T**2+69827.1*T**(-1); 1519.00 Y -28733.41+312.2648*T-48.0*T*LN(T)+1.656847E+30*T**(-9); 6000.00 N REF:2 ! FUNCTION GHSERSI 273.00 -8162.609+137.236859*T-22.8317533*T*LN(T) -0.001912904*T**2-3.552E-09*T**3+176667*T**(-1); 1687.00 Y -9457.642+167.281367*T-27.196*T*LN(T)-4.20369E+30*T**(-9); 6000.00 N REF:2 ! FUNCTION GHSERSR 273.00 -7532.367+107.183879*T-23.905*T*LN(T) -0.00461225*T**2-1.67477E-07*T**3-2055*T**(-1); 819.99 Y -13380.102+153.196104*T-30.0905432*T*LN(T)-0.003251266*T**2 +1.84189E-07*T**3+850134*T**(-1); 6000.00 N REF:2 ! FUNCTION GHSERZN 273.00 -7285.787+118.470069*T-23.701314*T*LN(T) -0.001712034*T**2-1.264963E-06*T**3; 692.68 Y -11070.559+172.34566*T-31.38*T*LN(T)+4.70514E+26*T**(-9); 6000.00 N REF:2 ! $ $ Other functions than SER $ bcc_a2 FUNCTION GBCCAL 273.00 +10083-4.813*T+GHSERAL#; 6000.00 N REF:0 ! FUNCTION GBCCCA 273.00 -7020.852+142.970155*T-28.2541*T*LN(T) +7.2326E-03*T**2-4.500217E-06*T**3+60578*T**(-1); 716.00 Y +1640.475+1.999694*T-6.276*T*LN(T)-16.1921E-03*T**2 -523000*T**(-1); 1115.00 Y -142331.096+1023.549046*T-143.8726979*T*LN(T)+32.543127E-03*T**2 -1.704079E-06*T**3+25353771*T**(-1); 6000.00 N REF:0 ! FUNCTION GBCCMN 273.00 -3235.3+127.85*T-23.7*T*LN(T) -0.00744271*T**2+60000*T**(-1); 1519.00 Y -23188.83+307.7043*T-48*T*LN(T)+1.265152E+30*T**(-9); 6000.00 N REF:2 ! FUNCTION GBCCZN 273.00 +2886.96-2.5104*T+GHSERZN#; 6000.00 N REF:0 ! $ liquid FUNCTION GLIQAL 273.00 +11005.029-11.841867*T+7.934E-20*T**7 +GHSERAL#; 9.33470E+02 Y +10482.382-11.253974*T+1.231E+28*T**(-9)+GHSERAL#; 6000.00 N REF:2 ! $ $************************************************************************** $************************************************************************** $ $ D) Thermodynamic descriptions of phases $ $************************************************************************** $************************************************************************** $ $########################################################################## $ THERMODYNAMIC DATA: LIQUID $########################################################################## $ PHASE LIQUID % 1 1.0 > Random substitutional model. >> 5 ! CONSTITUENT LIQUID :AL,CA,MG,MN,SR,SI,ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(LIQUID,AL;0) 273.00 +GLIQAL#; 6000.00 N REF:2 ! PARAMETER G(LIQUID,CA;0) 273.00 +10799.908-10.310466*T+GHSERCA#; 500.00 Y +7838.856+18.2979*T-8.9874787*T*LN(T)-0.02266537*T**2+3.338303E-06*T**3 -230193*T**(-1); 1115.00 Y -2654.938+188.9223*T-35*T*LN(T); 6000.00 N REF:2 ! PARAMETER G(LIQUID,MG;0) 273.00 +8202.243-8.83693*T+GHSERMG# -8.0176E-20*T**7; 923.00 Y +8690.316-9.392158*T+GHSERMG#-1.038192E+28*T**(-9); 6000.00 N REF:2 ! PARAMETER G(LIQUID,MN;0) 273.00 +17859.91-12.6208*T -4.419297E-21*T**7+GHSERMN#; 1519.00 Y +18739.51-13.2288*T-1.656847E+30*T**(-9)+GHSERMN#; 6000.00 N REF:0 ! PARAMETER G(LIQUID,SI;0) 273.00 +50696.36-30.099439*T +2.0931E-21*T**7+GHSERSI#; 1687.00 Y +49828.165-29.559068*T+4.2037E+30*T**(-9)+GHSERSI#; 6000.00 N REF:0 ! PARAMETER G(LIQUID,SR;0) 273.00 +2194.997-10.118994*T -5.0668978*T*LN(T)-0.031840595*T**2+4.981237E-06*T**3 -265559*T**(-1); 1050.00 Y -10855.29+213.406219*T-39.463*T*LN(T); 6000.00 N REF:2 ! PARAMETER G(LIQUID,ZN;0) 273.00 -128.574+108.177079*T -23.701314*T*LN(T)-0.001712034*T**2-1.264963E-06*T**3 -3.58958E-19*T**7; 692.68 Y -3620.391+161.608594*T-31.38*T*LN(T); 6000.00 N REF:2 ! $ $*************************************************************************** $ binary interaction parameters $*************************************************************************** PARAMETER L(LIQUID,AL,CA;0) 273.00 -89545+26.368*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,AL,CA;1) 273.00 -21847+11.769*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,AL,CA;2) 273.00 +4780+5.03*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,AL,MG;0) 273.00 -9031.5816+4.8547124*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,AL,MG;1) 273.00 -891.11184+1.1368285*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,AL,MG;2) 273.00 +434.02777; 6000.00 N REF:2 ! PARAMETER L(LIQUID,AL,MN;0) 273.00 -70584.9+28.22693*T; 6000.00 N REF:1 ! PARAMETER L(LIQUID,AL,MN;1) 273.00 -13293.5+9.82551*T; 6000.00 N REF:1 ! PARAMETER L(LIQUID,AL,SI;0) 273.00 -11340.10-1.23394*T; 6000.00 N REF:3 ! PARAMETER L(LIQUID,AL,SI;1) 273.00 -3530.93+1.35993*T; 6000.00 N REF:3 ! PARAMETER L(LIQUID,AL,SI;2) 273.00 +2265.39; 6000.00 N REF:3 ! PARAMETER L(LIQUID,AL,SR;0) 273.00 -74838.825+23.685781*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,AL,SR;1) 273.00 -31789.528+8.5492175*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,AL,SR;2) 273.00 +10682.821-4.1297796*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,AL,ZN;0) 273.00 +10465.55-3.39259*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,CA,MG;0) 273.00 -32000+18.3*T; 6000.00 N REF:pov14 ! PARAMETER L(LIQUID,CA,MG;1) 273.00 +60.3+6.549*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,CA,MG;2) 273.00 -5742.3+2.7596*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,CA,SR;0) 273.00 +1682; 6000.00 N REF:2 ! PARAMETER L(LIQUID,CA,SR;1) 273.00 +521; 6000.00 N REF:2 ! PARAMETER L(LIQUID,CA,SR;2) 273.00 -1145; 6000.00 N REF:2 ! PARAMETER L(LIQUID,CA,ZN;0) 273.00 -65435+10.624*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,CA,ZN;1) 273.00 +43288-12.978*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,CA,ZN;2) 273.00 -49709+35.547*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,MG,MN;0) 273.00 +19125.0+12.5*T; 6000.00 N REF:3 ! PARAMETER L(LIQUID,MG,SI;0) 273.00 -70000+22*T; 6000.00 N REF:pov14 ! PARAMETER L(LIQUID,MG,SI;1) 273.00 -3500; 6000.00 N REF:pov14 ! PARAMETER L(LIQUID,MG,SI;2) 273.00 +7500; 6000.00 N REF:pov14 ! PARAMETER L(LIQUID,MG,SR;0) 273.00 -18647.125+9.0704859*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,MG,SR;1) 273.00 -12831.602+7.5093935*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,MG,SR;2) 273.00 +1e-8; 6000.00 N REF:2 ! PARAMETER L(LIQUID,MG,ZN;0) 273.00 -77000+680*T -95.5*T*LN(T)+0.04*T**2; 6000.00 N REF:pov14 ! PARAMETER L(LIQUID,MG,ZN;1) 273.00 +3700+1.5*T; 6000.00 N REF:pov14 ! PARAMETER L(LIQUID,MG,ZN;2) 273.00 +1000; 6000.00 N REF:pov14 ! PARAMETER L(LIQUID,MN,SI;1) 273.00 -34917+3.205*T; 6000.00 N REF:4 ! PARAMETER L(LIQUID,MN,SI;2) 273.00 +46782-18.19*T; 6000.00 N REF:4 ! PARAMETER L(LIQUID,MN,SI;3) 273.00 +16168; 6000.00 N REF:4 ! PARAMETER L(LIQUID,MN,ZN;0) 273.00 -4666; 6000.00 N REF:5 ! PARAMETER L(LIQUID,MN,ZN;1) 273.00 +3500; 6000.00 N REF:pov13 ! PARAMETER L(LIQUID,SI,ZN;0) 273.00 +7829.25; 6000.00 N REF:3 ! PARAMETER L(LIQUID,SI,ZN;1) 273.00 -3338.18; 6000.00 N REF:3 ! PARAMETER L(LIQUID,SI,ZN;2) 273.00 -891.33; 6000.00 N REF:3 ! PARAMETER L(LIQUID,SR,ZN;0) 273.00 -66273+28.606*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,SR,ZN;1) 273.00 +37071-1.386*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,SR,ZN;2) 273.00 -16672.675; 6000.00 N REF:2 ! $ $*************************************************************************** $ ternary interaction parameters $*************************************************************************** PARAMETER L(LIQUID,AL,CA,MG;0) 273.00 -20000; 6000.00 N REF:pov14 ! PARAMETER L(LIQUID,AL,MG,MN;0) 273.00 +28000; 6000.00 N REF:1 ! PARAMETER L(LIQUID,AL,MG,MN;1) 273.00 +1e-8; 6000.00 N REF:1 ! PARAMETER L(LIQUID,AL,MG,MN;2) 273.00 +1e-8; 6000.00 N REF:1 ! PARAMETER L(LIQUID,AL,MG,SI;0) 273.00 +11882; 6000.00 N REF:6 ! PARAMETER L(LIQUID,AL,MG,SI;1) 273.00 -24207; 6000.00 N REF:6 ! PARAMETER L(LIQUID,AL,MG,SI;2) 273.00 -38223; 6000.00 N REF:6 ! PARAMETER L(LIQUID,AL,MG,ZN;0) 273.00 -11475+11*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,AL,MG,ZN;1) 273.00 -11475+11*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,AL,MG,ZN;2) 273.00 -11475+11*T; 6000.00 N REF:2 ! PARAMETER L(LIQUID,AL,MN,SI;0) 273.00 -72818; 6000.00 N REF:7 ! PARAMETER L(LIQUID,AL,MN,SI;1) 273.00 -16967; 6000.00 N REF:7 ! PARAMETER L(LIQUID,AL,MN,SI;2) 273.00 -55992; 6000.00 N REF:7 ! PARAMETER L(LIQUID,CA,MG,ZN;0) 273.00 -7019.7; 6000.00 N REF:12 ! PARAMETER L(LIQUID,CA,MG,ZN;1) 273.00 -47787; 6000.00 N REF:12 ! PARAMETER L(LIQUID,CA,MG,ZN;2) 273.00 -5437.5; 6000.00 N REF:12 ! PARAMETER L(LIQUID,MG,SI,ZN;0) 273.00 -118047.9+91.62*T; 6000.00 N REF:11 ! $ $########################################################################## $ THERMODYNAMIC PARAMETERS: HCP_A3 $########################################################################## $ TYPE_DEFINITION + GES A_P_D HCP_A3 MAGNETIC -3.0 0.28 ! PHASE HCP_A3 %+ 2 1 .5 > Mg-Matrix phase, hexagonal close-packed. >> 5 ! CONSTITUENT HCP_A3 :AL,CA,MG%,MN,SI,SR,ZN : VA : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(HCP_A3,AL:VA;0) 273.00 +5481-1.8*T+GHSERAL#; 6000.00 N REF:0 ! PARAMETER G(HCP_A3,CA:VA;0) 273.00 +500+0.7*T+GHSERCA#; 6000.00 N REF:0 ! PARAMETER G(HCP_A3,MG:VA;0) 273.00 +GHSERMG#; 6000.00 N REF:0 ! PARAMETER G(HCP_A3,MN:VA;0) 273.00 -4439.3+133.007*T-24.5177*T*LN(T) -0.006*T**2+69600*T**(-1); 1519.00 Y -27070.1+310.7894*T-48*T*LN(T)+3.86196E+30*T**(-9); 6000.00 N REF:0 ! PARAMETER G(HCP_A3,SI:VA;0) 273.00 +49200-20.8*T+GHSERSI#; 6000.00 N REF:0 ! PARAMETER G(HCP_A3,SR:VA;0) 273.00 +250+0.7*T+GHSERSR#; 6000.00 N REF:0 ! PARAMETER G(HCP_A3,ZN:VA;0) 273.00 +2970-1.57*T+GHSERZN#; 6000.00 N REF:0 ! $ $*************************************************************************** $ binary interaction parameters $*************************************************************************** PARAMETER L(HCP_A3,AL,MG:VA;0) 273.00 +4271.9648-2.1898692*T; 6000.00 N REF:2 ! PARAMETER L(HCP_A3,AL,MG:VA;1) 273.00 -1.076864+1.014848*T; 6000.00 N REF:2 ! PARAMETER L(HCP_A3,AL,MG:VA;2) 273.00 -965.93125; 6000.00 N REF:2 ! PARAMETER L(HCP_A3,AL,MN:VA;0) 273.00 -108066+43.83*T; 6000.00 N REF:3 ! PARAMETER L(HCP_A3,AL,MN:VA;1) 273.00 -54519.8+40*T; 6000.00 N REF:3 ! PARAMETER L(HCP_A3,AL,SI:VA;0) 273.00 +4000; 6000.00 N REF:9 ! PARAMETER L(HCP_A3,AL,ZN:VA;0) 273.00 +18820.95-8.95255*T; 6000.00 N REF:2 ! PARAMETER L(HCP_A3,AL,ZN:VA;1) 273.00 +1E-06; 6000.00 N REF:2 ! PARAMETER L(HCP_A3,AL,ZN:VA;2) 273.00 +1E-06; 6000.00 N REF:2 ! PARAMETER L(HCP_A3,AL,ZN:VA;3) 273.00 -702.79; 6000.00 N REF:2 ! PARAMETER L(HCP_A3,CA,MG:VA;0) 273.00 -9183.2+16.981*T; 6000.00 N REF:2 ! PARAMETER L(HCP_A3,CA,SR:VA;0) 273.00 +3770; 6000.00 N REF:2 ! PARAMETER L(HCP_A3,CA,SR:VA;1) 273.00 +877; 6000.00 N REF:2 ! PARAMETER L(HCP_A3,CA,SR:VA;2) 273.00 -1125; 6000.00 N REF:2 ! PARAMETER L(HCP_A3,MG,MN:VA;0) 273.00 +32985.0+2.5*T; 6000.00 N REF:3 ! PARAMETER L(HCP_A3,MG,SI:VA;0) 273.00 -7148.79+0.89361*T; 6000.00 N REF:3 ! PARAMETER L(HCP_A3,MG,SR:VA;0) 273.00 +10000; 6000.00 N REF:2 ! PARAMETER L(HCP_A3,MG,SR:VA;1) 273.00 +1e-8; 6000.00 N REF:2 ! PARAMETER L(HCP_A3,MG,ZN:VA;0) 273.00 -3056.82+5.63801*T; 6000.00 N REF:4 ! PARAMETER L(HCP_A3,MG,ZN:VA;1) 273.00 -3127.26+5.65563*T; 6000.00 N REF:4 ! PARAMETER L(HCP_A3,MN,ZN:VA;0) 273.00 -15000+3.9*T; 6000.00 N REF:16 ! PARAMETER L(HCP_A3,MN,ZN:VA;1) 273.00 +21000-9*T; 6000.00 N REF:16 ! PARAMETER L(HCP_A3,SI,ZN:VA;0) 273.00 +80*T; 6000.00 N REF:3 ! PARAMETER L(HCP_A3,AL,CA,MG:VA;0) 273.00 +1e-8; 6000.00 N REF:pov14 ! PARAMETER L(HCP_A3,AL,MG,MN:VA;0) 273.00 +1e-8; 6000.00 N REF:pov14 ! PARAMETER L(HCP_A3,AL,MG,MN:VA;1) 273.00 +1e-8; 6000.00 N REF:pov14 ! PARAMETER L(HCP_A3,AL,MG,MN:VA;2) 273.00 +1e-8; 6000.00 N REF:pov14 ! $ $*************************************************************************** $ magnetic parameters $*************************************************************************** PARAMETER TC(HCP_A3,MN:VA;0) 273.00 +540; 6000.00 N REF:0 ! PARAMETER BMAGN(HCP_A3,MN:VA;0) 273.00 +0.62; 6000.00 N REF:0 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: HCP_ZN $########################################################################### $ PHASE HCP_ZN % 2 1 .5 > Hexagonal close-packed. >> 2 ! CONSTITUENT HCP_ZN :AL,MG,MN,SI,ZN% : VA : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(HCP_ZN,AL:VA;0) 273.00 +5482-1.8*T+GHSERAL#; 6000.00 N REF:2 ! PARAMETER G(HCP_ZN,MG:VA;0) 273.00 +100+GHSERMG#; 6000.00 N REF:2 ! PARAMETER G(HCP_ZN,MN:VA;0) 273.00 -4439.3+133.007*T-24.5177*T*LN(T) -0.006*T**2+69600*T**(-1); 1519.00 Y -27070.1+310.7894*T-48*T*LN(T)+3.86196E+30*T**(-9); 6000.00 N REF:0 ! PARAMETER G(HCP_ZN,SI:VA;0) 273.00 +49201-20.8*T+GHSERSI#; 6000.00 N REF:3 ! PARAMETER G(HCP_ZN,ZN:VA;0) 273.00 +GHSERZN#; 6000.00 N REF:2 ! $ $*************************************************************************** $ binary interaction parameters $*************************************************************************** PARAMETER L(HCP_ZN,AL,MG:VA;0) 273.00 +1950-2*T; 6000.00 N REF:2 ! PARAMETER L(HCP_ZN,AL,MG:VA;1) 273.00 +1480-2.08*T; 6000.00 N REF:2 ! PARAMETER L(HCP_ZN,AL,MG:VA;2) 273.00 +3500; 6000.00 N REF:2 ! PARAMETER L(HCP_ZN,AL,ZN:VA;0) 273.00 +18820.95-8.95255*T; 6000.00 N REF:2 ! PARAMETER L(HCP_ZN,AL,ZN:VA;1) 273.00 +1E-06; 6000.00 N REF:2 ! PARAMETER L(HCP_ZN,AL,ZN:VA;2) 273.00 +1E-06; 6000.00 N REF:2 ! PARAMETER L(HCP_ZN,AL,ZN:VA;3) 273.00 -702.79; 6000.00 N REF:2 ! PARAMETER L(HCP_ZN,MG,MN:VA;0) 273.00 +32985.0+2.5*T; 6000.00 N REF:3 ! PARAMETER L(HCP_ZN,MG,ZN:VA;0) 273.00 -3056.82+5.63801*T; 6000.00 N REF:2 ! PARAMETER L(HCP_ZN,MG,ZN:VA;1) 273.00 -3127.26+5.65563*T; 6000.00 N REF:2 ! $ $*************************************************************************** $ ternary interaction parameters $*************************************************************************** PARAMETER L(HCP_ZN,AL,MG,ZN:VA;0) 273.00 +1E-04; 6000.00 N REF:2 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: BCC_A2 $########################################################################### $ TYPE_DEFINITION ( GES A_P_D BCC_A2 MAGNETIC -1.0 0.4 ! PHASE BCC_A2 %( 2 1 3 > Body-centered cubic. >> 1 ! CONSTITUENT BCC_A2 :AL,CA,MG,MN%,SI,SR,ZN : VA : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(BCC_A2,AL:VA;0) 273.00 +GBCCAL#; 6000.00 N REF:0 ! PARAMETER G(BCC_A2,CA:VA;0) 273.00 -7020.852+142.970155*T -28.2541*T*LN(T)+0.0072326*T**2-4.500217E-06*T**3 +60578*T**(-1); 716.00 Y +1640.475+1.999694*T-6.276*T*LN(T)-0.0161921*T**2 -523000*T**(-1); 1115.00 Y -142331.096+1023.54905*T-143.872698*T*LN(T)+0.032543127*T**2 -1.704079E-06*T**3 +25353771*T**(-1); 6000.00 N REF:2 ! PARAMETER G(BCC_A2,MG:VA;0) 273.00 +3100-2.1*T+GHSERMG#; 6000.00 N REF:0 ! PARAMETER G(BCC_A2,MN:VA;0) 273.00 +GBCCMN#; 6000.00 N REF:0 ! PARAMETER G(BCC_A2,SI:VA;0) 273.00 +47000-22.5*T+GHSERSI#; 6000.00 N REF:0 ! PARAMETER G(BCC_A2,SR:VA;0) 273.00 -6779.234+116.583654*T -25.6708365*T*LN(T)-0.003126762*T**2+2.2965E-07*T**3 +27649*T**(-1); 819.99 Y -6970.594+122.067301*T-26.57*T*LN(T)-0.0019493*T**2-1.7895E-08*T**3 +16495*T**(-1); 1050.00 Y +8168.357+0.423037*T-9.7788593*T*LN(T)-0.009539908*T**2+5.20221E-07*T**3 -2414794*T**(-1); 6000.00 N REF:2 ! PARAMETER G(BCC_A2,ZN:VA;0) 273.00 +GBCCZN#; 6000.00 N REF:0 ! $ $*************************************************************************** $ binary interaction parameters $*************************************************************************** PARAMETER L(BCC_A2,AL,MN:VA;0) 273.00 -120077+52.851*T; 6000.00 N REF:3 ! PARAMETER L(BCC_A2,AL,MN:VA;1) 273.00 -40652+29.2764*T; 6000.00 N REF:3 ! PARAMETER L(BCC_A2,CA,MG:VA;0) 273.00 +100000; 6000.00 N REF:2 ! PARAMETER L(BCC_A2,CA,SR:VA;0) 273.00 +3770; 6000.00 N REF:2 ! PARAMETER L(BCC_A2,CA,SR:VA;1) 273.00 +877; 6000.00 N REF:2 ! PARAMETER L(BCC_A2,CA,SR:VA;2) 273.00 -1125; 6000.00 N REF:2 ! PARAMETER L(BCC_A2,MG,MN:VA;0) 273.00 +70000.0; 6000.00 N REF:3 ! PARAMETER L(BCC_A2,MG,SI:VA;0) 273.00 +1E-10; 6000.00 N REF:3 ! PARAMETER L(BCC_A2,MG,SR:VA;0) 273.00 +20000; 6000.00 N REF:2 ! PARAMETER L(BCC_A2,MG,SR:VA;1) 273.00 +1e-8 ; 6000.00 N REF:2 ! PARAMETER L(BCC_A2,MG,ZN:VA;0) 273.00 -10000; 6000.00 N REF:2 ! PARAMETER L(BCC_A2,MN,SI:VA;0) 273.00 -89620.7+2.94097*T; 6000.00 N REF:3 ! PARAMETER L(BCC_A2,MN,SI:VA;1) 273.00 -7500; 6000.00 N REF:3 ! PARAMETER L(BCC_A2,MN,ZN:VA;0) 273.00 -8200-0.75*T; 6000.00 N REF:5 ! PARAMETER L(BCC_A2,SI,ZN:VA;0) 273.00 +80*T; 6000.00 N REF:3 ! $ $*************************************************************************** $ magnetic parameters $*************************************************************************** PARAMETER TC(BCC_A2,MN:VA;0) 273.00 -580; 6000.00 N REF:8 ! PARAMETER BMAGN(BCC_A2,MN:VA;0) 273.00 -0.27; 6000.00 N REF:8 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: FCC_A1 $########################################################################### $ TYPE_DEFINITION * GES A_P_D FCC_A1 MAGNETIC -3.0 0.28 ! PHASE FCC_A1 %* 2 1 1 > Face-centered cubic. >> 1 ! CONSTITUENT FCC_A1 :AL%,CA,MG,MN,SI,SR,ZN : VA : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(FCC_A1,AL:VA;0) 273.00 +GHSERAL#; 6000.00 N REF:0 ! PARAMETER G(FCC_A1,CA:VA;0) 273.00 +GHSERCA#; 6000.00 N REF:2 ! PARAMETER G(FCC_A1,MG:VA;0) 273.00 +2600-0.9*T+GHSERMG#; 6000.00 N REF:0 ! PARAMETER G(FCC_A1,MN:VA;0) 273.00 -3439.3+131.884*T-24.5177*T*LN(T) -0.006*T**2+69600*T**(-1); 1519.00 Y -26070.1+309.6664*T-48*T*LN(T)+3.86196E+30*T**(-9); 6000.00 N REF:0 ! PARAMETER G(FCC_A1,SI:VA;0) 273.00 +51000-21.8*T+GHSERSI#; 6000.00 N REF:0 ! PARAMETER G(FCC_A1,SR:VA;0) 273.00 +GHSERSR#; 6000.00 N REF:0 ! PARAMETER G(FCC_A1,ZN:VA;0) 273.00 +2969.82-1.56968*T+GHSERZN#; 6000.00 N REF:0 ! $ $*************************************************************************** $ binary interaction parameters $*************************************************************************** PARAMETER L(FCC_A1,AL,MG:VA;0) 273.00 +1587.61+2.1413324*T; 6000.00 N REF:2 ! PARAMETER L(FCC_A1,AL,MG:VA;1) 273.00 +1179.5327-0.69523422*T; 6000.00 N REF:2 ! PARAMETER L(FCC_A1,AL,MG:VA;2) 273.00 -866.82189; 6000.00 N REF:2 ! PARAMETER L(FCC_A1,AL,MN:VA;0) 273.00 -69300+25.0000*T; 6000.00 N REF:3 ! PARAMETER L(FCC_A1,AL,MN:VA;1) 273.00 +8800.0; 6000.00 N REF:3 ! PARAMETER L(FCC_A1,AL,SI:VA;0) 273.00 -3143.78+0.39297*T; 6000.00 N REF:3 ! PARAMETER L(FCC_A1,AL,ZN:VA;0) 273.00 +7297.48+0.47512*T; 6000.00 N REF:2 ! PARAMETER L(FCC_A1,AL,ZN:VA;1) 273.00 +6612.88-4.5911*T; 6000.00 N REF:2 ! PARAMETER L(FCC_A1,AL,ZN:VA;2) 273.00 -3097.19+3.30635*T; 6000.00 N REF:2 ! PARAMETER L(FCC_A1,CA,MG:VA;0) 273.00 +100000; 6000.00 N REF:2 ! PARAMETER L(FCC_A1,CA,SR:VA;0) 273.00 +3770; 6000.00 N REF:2 ! PARAMETER L(FCC_A1,CA,SR:VA;1) 273.00 +877; 6000.00 N REF:2 ! PARAMETER L(FCC_A1,CA,SR:VA;2) 273.00 -1125; 6000.00 N REF:2 ! PARAMETER L(FCC_A1,MG,MN:VA;0) 273.00 +70000.0; 6000.00 N REF:3 ! PARAMETER L(FCC_A1,MG,SI:VA;0) 273.00 -7148.79+0.89361*T; 6000.00 N REF:3 ! PARAMETER L(FCC_A1,MG,SR:VA;0) 273.00 +20000; 6000.00 N REF:2 ! PARAMETER L(FCC_A1,MG,SR:VA;1) 273.00 +1e-8; 6000.00 N REF:2 ! PARAMETER L(FCC_A1,MG,ZN:VA;0) 273.00 -3056.82+5.63801*T; 6000.00 N REF:4 ! PARAMETER L(FCC_A1,MG,ZN:VA;1) 273.00 -3127.26+5.65563*T; 6000.00 N REF:4 ! PARAMETER L(FCC_A1,MN,SI:VA;0) 273.00 -95600+2.94097*T; 6000.00 N REF:3 ! PARAMETER L(FCC_A1,MN,SI:VA;1) 273.00 -7500; 6000.00 N REF:3 ! PARAMETER L(FCC_A1,MN,ZN:VA;0) 273.00 -9200; 6000.00 N REF:5 ! PARAMETER L(FCC_A1,SI,ZN:VA;0) 273.00 +80*T; 6000.00 N REF:3 ! $ $*************************************************************************** $ magnetic parameters $*************************************************************************** PARAMETER TC(FCC_A1,MN:VA;0) 273.00 +540; 6000.00 N REF:0 ! PARAMETER BMAGN(FCC_A1,MN:VA;0) 273.00 +0.62; 6000.00 N REF:0 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: ALPHA_MN $########################################################################### $ PHASE ALPHA_MN % 2 1 1 > BCC_A12 cubic. >> 1 ! CONSTITUENT ALPHA_MN :AL,MG,MN%,SI,ZN : VA : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(ALPHA_MN,AL:VA;0) 273.00 +10083.00-4.813*T+GHSERAL#; 6000.00 N REF:3 ! PARAMETER G(ALPHA_MN,MG:VA;0) 273.00 +4600+GHSERMG#; 6000.00 N REF:17 ! PARAMETER G(ALPHA_MN,MN:VA;0) 273.00 +GHSERMN#; 6000.00 N REF:0 ! PARAMETER G(ALPHA_MN,SI:VA;0) 273.00 +50208.0-20.377*T+GHSERSI#; 6000.00 N REF:3 ! PARAMETER G(ALPHA_MN,ZN:VA;0) 273.00 +3000+GHSERZN#; 6000.00 N REF:17 ! $ $*************************************************************************** $ binary interaction parameters $*************************************************************************** PARAMETER L(ALPHA_MN,AL,MN:VA;0) 273.00 -101410+43*T; 6000.00 N REF:3 ! PARAMETER L(ALPHA_MN,MG,MN:VA;0) 273.00 +70000; 6000.00 N REF:3 ! PARAMETER L(ALPHA_MN,MN,SI:VA;0) 273.00 -142743.62+22.3961*T; 6000.00 N REF:3 ! PARAMETER L(ALPHA_MN,MN,SI:VA;1) 273.00 +16440.608-3.53*T; 6000.00 N REF:3 ! PARAMETER L(ALPHA_MN,MN,ZN:VA;0) 273.00 +5000; 6000.00 N REF:16 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: BETA_MN $########################################################################### $ PHASE BETA_MN % 2 1 1 > cubic A13. >> 2 ! CONSTITUENT BETA_MN :AL,MG,MN%,SI,ZN : VA : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(BETA_MN,AL:VA;0) 273.00 +10920.44-4.8116*T+GHSERAL#; 6000.00 N REF:3 ! PARAMETER G(BETA_MN,MG:VA;0) 273.00 +4600+GHSERMG#; 6000.00 N REF:17 ! PARAMETER G(BETA_MN,MN:VA;0) 273.00 +2314.88+5.936*T-1.4203*T*LN(T) +1.51409E-03*T**2+442.0*T**(-1)+GHSERMN#; 1519.00 Y +442.65-0.9715*T+2.3107229E+30*T**(-9)+GHSERMN#; 6000.00 N REF:0 ! PARAMETER G(BETA_MN,SI:VA;0) 273.00 +47279.0-20.377*T+GHSERSI#; 6000.00 N REF:3 ! PARAMETER G(BETA_MN,ZN:VA;0) 273.00 +2000+GHSERZN#; 6000.00 N REF:16 ! $ $*************************************************************************** $ binary interaction parameters $*************************************************************************** PARAMETER L(BETA_MN,AL,MN:VA;0) 273.00 -119022+52.507*T; 6000.00 N REF:3 ! PARAMETER L(BETA_MN,AL,MN:VA;1) 273.00 -1763; 6000.00 N REF:3 ! PARAMETER L(BETA_MN,MG,MN:VA;0) 273.00 +70000; 6000.00 N REF:3 ! PARAMETER L(BETA_MN,MN,SI:VA;0) 273.00 -142343.62+21.89261*T; 6000.00 N REF:3 ! PARAMETER L(BETA_MN,MN,SI:VA;1) 273.00 +16440.608-3.53*T; 6000.00 N REF:3 ! PARAMETER L(BETA_MN,MN,ZN:VA;0) 273.00 -5200; 6000.00 N REF:16 ! PARAMETER L(BETA_MN,MN,ZN:VA;1) 273.00 -3000; 6000.00 N REF:16 ! $ $*************************************************************************** $ ternary interaction parameters $*************************************************************************** $########################################################################### $ THERMODYNAMIC PARAMETERS: ALMG_BETA $########################################################################### $ PHASE ALMG_BETA % 2 89 140 > Cubic, space group Fd3-m. >> 2 ! CONSTITUENT ALMG_BETA :MG : AL%,ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(ALMG_BETA,MG:AL;0) 273.00 -809136.27+115.01663*T +89*GHSERMG#+140*GHSERAL#; 6000.00 N REF:2 ! PARAMETER G(ALMG_BETA,MG:ZN;0) 273.00 +206100+89*GHSERMG# +140*GHSERZN#; 6000.00 N REF:2 ! $ $*************************************************************************** $ interaction parameters $*************************************************************************** PARAMETER L(ALMG_BETA,MG:AL,ZN;0) 273.00 -1717500+343.5*T; 6000.00 N REF:2 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: ALMG_EPS $########################################################################### $ PHASE ALMG_EPS % 2 23 30 > Trigonal, space group R3-. >> 2 ! CONSTITUENT ALMG_EPS :MG : AL%,ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(ALMG_EPS,MG:AL;0) 273.00 -172080.69-5.8490582*T +23*GHSERMG#+30*GHSERAL#; 6000.00 N REF:2 ! PARAMETER G(ALMG_EPS,MG:ZN;0) 273.00 -318000+63.6*T+23*GHSERMG# +30*GHSERZN#; 6000.00 N REF:2 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: G_AL12MG17 $########################################################################### $ PHASE G_AL12MG17 % 3 5 12 12 > Gamma equilibrium phase, space group: I43m, prototype: Alpha-Mn. Main precipitate in AZ Mg-alloys. [REF:e.g. C4,C5,C6,C7] >> 4 ! CONSTITUENT G_AL12MG17 :MG : AL,CA,MG%,ZN : AL%,MG,ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(G_AL12MG17,MG:AL:AL;0) 273.00 +8360+20.338857*T +5*GHSERMG#+24*GHSERAL#; 6000.00 N REF:2 ! PARAMETER G(G_AL12MG17,MG:CA:AL;0) 273.00 -325000+35*T +5*GHSERMG#+12*GHSERCA#+12*GHSERAL#; 6000.00 N REF:14 ! PARAMETER G(G_AL12MG17,MG:CA:MG;0) 273.00 +50000 +5*GHSERMG#+12*GHSERCA#+12*GHSERMG#; 6000.00 N REF:14 ! PARAMETER G(G_AL12MG17,MG:CA:ZN;0) 273.00 +100000 +5*GHSERMG#+12*GHSERCA#+12*GHSERZN#; 6000.00 N REF:pov14 ! PARAMETER G(G_AL12MG17,MG:MG:AL;0) 273.00 -104308.83+23.495281*T +17*GHSERMG#+12*GHSERAL#; 6000.00 N REF:2 ! PARAMETER G(G_AL12MG17,MG:ZN:AL;0) 273.00 -87000+58*T+5*GHSERMG# +12*GHSERAL#+12*GHSERZN#; 6000.00 N REF:2 ! PARAMETER G(G_AL12MG17,MG:AL:MG;0) 273.00 +180556-138.069*T +17*GHSERMG#+12*GHSERAL#; 6000.00 N REF:2 ! PARAMETER G(G_AL12MG17,MG:MG:MG;0) 273.00 +139371-87.319*T +29*GHSERMG#; 6000.00 N REF:2 ! PARAMETER G(G_AL12MG17,MG:ZN:MG;0) 273.00 +87000+29*T+17*GHSERMG# +12*GHSERZN#; 6000.00 N REF:2 ! PARAMETER G(G_AL12MG17,MG:AL:ZN;0) 273.00 +14.5*T+5*GHSERMG# +12*GHSERAL#+12*GHSERZN#; 6000.00 N REF:2 ! PARAMETER G(G_AL12MG17,MG:MG:ZN;0) 273.00 -145000+58*T+17*GHSERMG# +12*GHSERZN#; 6000.00 N REF:2 ! PARAMETER G(G_AL12MG17,MG:ZN:ZN;0) 273.00 +290000+5*GHSERMG# +24*GHSERZN#; 6000.00 N REF:2 ! $ $*************************************************************************** $ interaction parameters $*************************************************************************** PARAMETER L(G_AL12MG17,MG:AL:AL,MG;0) 273.00 +113100-14.5*T; 6000.00 N REF:2 ! PARAMETER L(G_AL12MG17,MG:CA,MG:AL;0) 273.00 -543434+25*T; 6000.00 N REF:2 ! PARAMETER L(G_AL12MG17,MG:MG,ZN:AL;0) 273.00 -116000+58*T; 6000.00 N REF:2 ! PARAMETER L(G_AL12MG17,MG:MG:AL,MG;0) 273.00 +113100-14.5*T; 6000.00 N REF:2 ! PARAMETER L(G_AL12MG17,MG:ZN:AL,MG;0) 273.00 +113100-14.5*T; 6000.00 N REF:2 ! PARAMETER L(G_AL12MG17,MG:MG,ZN:MG;0) 273.00 -116000+58*T; 6000.00 N REF:2 ! PARAMETER L(G_AL12MG17,MG:MG,ZN:ZN;0) 273.00 -116000+58*T; 6000.00 N REF:2 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: ALMGMN_T $########################################################################### $ PHASE ALMGMN_T % 3 0.78261 0.130435 0.08696 > Cubic, space group Fd3-m. >> 2 ! CONSTITUENT ALMGMN_T : AL : MG : MN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(ALMGMN_T,AL:MG:MN;0) 273.00 -8652.17 +0.78261*GHSERAL#+0.130435*GHSERMG#+0.086957*GHSERMN#; 6000.00 N REF:1 ! $ $########################################################################### $ THERMODYNAMIC DATA: AL4MN $########################################################################### $ PHASE AL4MN % 2 4 1 > Hexagonal >> 1 ! CONSTITUENT AL4MN : AL : MN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(AL4MN,AL:MN;0) 273.00 -100005+30*T+4*GHSERAL# +GHSERMN#; 6000.00 N REF:3 ! $ $########################################################################### $ THERMODYNAMIC DATA: AL6MN $########################################################################### PHASE AL6MN % 2 0.857143 0.142857 > Orthorhombic equilibrium phase with 28 atoms per unit cell. >> 2 ! CONSTITUENT AL6MN : AL : MN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(AL6MN,AL:MN;0) 273.00 -17794.9+7.6656*T +0.857143*GHSERAL#+0.142857*GHSERMN#; 6000.00 N REF:3 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: AL8MN5_D810 $########################################################################### $ PHASE AL8MN5_D810 % 3 12 4 10 > First solid phase forming during casting of AZ alloy. [REF:C2] Also found as heterogeneous precipitate in AZ61 [REF:C3] >> 3 ! CONSTITUENT AL8MN5_D810 : AL%,SI : MN : AL,MN,ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(AL8MN5_D810,AL:MN:AL;0) 273.00 -308671+56.6488*T+22*GHSERAL# +4*GHSERMN#; 6000.00 N REF:3 ! PARAMETER G(AL8MN5_D810,AL:MN:MN;0) 273.00 -596866.4+94.61192*T+12*GHSERAL# +14*GHSERMN#; 6000.00 N REF:3 ! PARAMETER G(AL8MN5_D810,AL:MN:ZN;0) 273.00 -250000+12*GHSERAL# +4*GHSERMN#+10*GHSERZN#; 6000.00 N REF:pov14 ! PARAMETER G(AL8MN5_D810,SI:MN:MN;0) 273.00 +14*GHSERMN# +12*GHSERSI#; 6000.00 N REF:3 ! PARAMETER G(AL8MN5_D810,SI:MN:ZN;0) 273.00 +12*GHSERSI# +4*GHSERMN#+10*GHSERZN#; 6000.00 N REF:pov14 ! PARAMETER G(AL8MN5_D810,SI:MN:AL;0) 273.00 +10*GHSERAL#+4*GHSERMN# +12*GHSERSI#; 6000.00 N REF:3 ! $ $*************************************************************************** $ interaction parameters $*************************************************************************** PARAMETER L(AL8MN5_D810,AL:MN:AL,MN;0) 273.00 -546234+387.348*T; 6000.00 N REF:3 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: AL11MN4 $########################################################################### $ PHASE AL11MN4 % 2 11 4 > Triclinic. Forms during solidification of AZ alloys. [REF:C6] >> 3 ! CONSTITUENT AL11MN4 : AL : MN,ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(AL11MN4,AL:MN;0) 273.00 -354690+103.03095*T+11*GHSERAL# +4*GHSERMN#; 6000.00 N REF:3 ! PARAMETER G(AL11MN4,AL:ZN;0) 273.00 +11*GHSERAL#+4*GHSERZN#; 6000.00 N REF:pov14 ! $ $*************************************************************************** $ interaction parameters $*************************************************************************** PARAMETER G(AL11MN4,AL:MN,ZN;0) 273.00 -40000; 6000.00 N REF:pov14 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: AL12MN $########################################################################### $ PHASE AL12MN % 2 1 0.08333 > Body-centered cubic. >> 2 ! CONSTITUENT AL12MN : AL : MN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(AL12MN,AL:MN;0) 273.00 -8491.5+2.8305*T+GHSERAL# +0.08333*GHSERMN#; 6000.00 N REF:1 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: AL3X8 $########################################################################### $ PHASE AL3X8 % 2 3 8 > >> 1 ! CONSTITUENT AL3X8 :AL : CA,MG,SR : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(AL3X8,AL:CA;0) 273.00 -194475+44.784*T+8*GHSERCA# +3*GHSERAL#; 6000.00 N REF:2 ! PARAMETER G(AL3X8,AL:MG;0) 273.00 +55000+8*GHSERMG# +3*GHSERAL#; 6000.00 N REF:14 ! PARAMETER G(AL3X8,AL:SR;0) 273.00 -106783.29-23.649504*T+3*GHSERAL# +8*GHSERSR#; 6000.00 N REF:2 ! PARAMETER L(AL3X8,AL:CA,MG;0) 273.00 -275000+55*T; 6000.00 N REF:14 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: AL4X $########################################################################### $ PHASE AL4X % 2 4 1 > >> 1 ! CONSTITUENT AL4X :AL,MG : CA,SR : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(AL4X,AL:CA;0) 273.00 -100170+20.197*T+4*GHSERAL# +GHSERCA#; 6000.00 N REF:2 ! PARAMETER G(AL4X,AL:SR;0) 273.00 -133430.53+34.227586*T+4*GHSERAL# +GHSERSR#; 6000.00 N REF:2 ! PARAMETER G(AL4X,MG:CA;0) 273.00 -30000+4*GHSERMG# +GHSERCA#; 6000.00 N REF:14 ! PARAMETER G(AL4X,MG:SR;0) 273.00 +4*GHSERMG# +GHSERSR#+50000; 6000.00 N REF:pov14 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: AL14CA13 $########################################################################### $ PHASE AL14CA13 % 2 14 13 > >> 1 ! CONSTITUENT AL14CA13 :AL : CA : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(AL14CA13,AL:CA;0) 273.00 -725000+137.5*T+14*GHSERAL# +13*GHSERCA#; 6000.00 N REF:pov14 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: AL2SR $########################################################################### $ PHASE AL2SR % 2 2 1 > >> 1 ! CONSTITUENT AL2SR :AL : SR : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(AL2SR,AL:SR;0) 273.00 -83468.037+18.320025*T +2*GHSERAL#+GHSERSR#; 6000.00 N REF:2 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: AL7SR8 $########################################################################### $ PHASE AL7SR8 % 2 7 8 > >> 1 ! CONSTITUENT AL7SR8 :AL : SR : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(AL7SR8,AL:SR;0) 273.00 -312195.78+47.25709*T +7*GHSERAL#+8*GHSERSR#; 6000.00 N REF:2 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: C2M5Z13 $########################################################################### $ PHASE C2M5Z13 % 3 2 5 13 > >> 1 ! CONSTITUENT C2M5Z13 :CA : MG : ZN : ! PARAMETER G(C2M5Z13,CA:MG:ZN;0) 273.00 -300000+15*T+2*GHSERCA# +13*GHSERZN#+5*GHSERMG#; 6.00000E+03 N REF:12 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: C2M6Z3 $########################################################################### $ PHASE C2M6Z3 % 3 2 6 3 > ternary intermetallic Ca2Mg6Zn3 precipitate, stoichiometric variant of IM1 phase. >> 2 ! CONSTITUENT C2M6Z3 :CA : MG : ZN : ! PARAMETER G(C2M6Z3,CA:MG:ZN;0) 273.00 -139077-0.8081*T+2*GHSERCA# +3*GHSERZN#+6*GHSERMG#; 6.00000E+03 N REF:12 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: CAZN $########################################################################### $ PHASE CAZN % 2 0.5 0.5 > >> 1 ! CONSTITUENT CAZN :CA : ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(CAZN,CA:ZN;0) 273.00 -17842.54+0.53*T +0.5*GHSERCA#+0.5*GHSERZN#; 6000.00 N REF:pov14 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: CAZN2 $########################################################################### $ PHASE CAZN2 % 2 0.33333 0.66667 > >> 1 ! CONSTITUENT CAZN2 :CA,SR : ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(CAZN2,CA:ZN;0) 273.00 -22728+1.48*T +0.33333*GHSERCA#+0.66667*GHSERZN#; 6000.00 N REF:pov14 ! PARAMETER G(CAZN2,SR:ZN;0) 273.00 -22852.67+6.214*T +0.33333*GHSERSR#+0.66667*GHSERZN#; 6000.00 N REF:2 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: CAZN3 $########################################################################### $ PHASE CAZN3 % 2 0.25 0.75 > >> 1 ! CONSTITUENT CAZN3 :CA : ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(CAZN3,CA:ZN;0) 273.00 -21418.76+2.66*T+0.25*GHSERCA# +0.75*GHSERZN#; 6000.00 N REF:pov14 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: CAZN5 $########################################################################### $ PHASE CAZN5 % 2 0.1666667 0.8333333 > >> 1 ! CONSTITUENT CAZN5 :CA,SR : ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(CAZN5,CA:ZN;0) 273.00 -19997.5+3.84*T +0.1666667*GHSERCA#+0.8333333*GHSERZN#; 6000.00 N REF:pov14 ! PARAMETER G(CAZN5,SR:ZN;0) 273.00 -20330.83+5.229*T +0.1666667*GHSERSR#+0.8333333*GHSERZN#; 6000.00 N REF:2 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: CAZN11 $########################################################################### $ PHASE CAZN11 % 2 0.083333 0.916667 > >> 1 ! CONSTITUENT CAZN11 :CA : MG,ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(CAZN11,CA:ZN;0) 273.00 -14939.82+3.79*T+0.083333*GHSERCA# +0.916667*GHSERZN#; 6000.00 N REF:13 ! PARAMETER G(CAZN11,CA:MG;0) 273.00 -978.08+13.26*T+0.083333*GBCCCA# +0.916667*GHSERMG#; 6000.00 N REF:13 ! $ $*************************************************************************** $ interaction parameters $*************************************************************************** PARAMETER L(CAZN11,CA:MG,ZN;0) 273.00 -20000; 6000.00 N REF:pov14 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: CAZN13 $########################################################################### $ PHASE CAZN13 % 2 0.071429 0.928571 > >> 1 ! CONSTITUENT CAZN13 :CA,SR : MG,ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(CAZN13,CA:ZN;0) 273.00 -14046.29+4.14*T+0.071429*GBCCCA# +0.928571*GHSERZN#; 6000.00 N REF:13 ! PARAMETER G(CAZN13,CA:MG;0) 273.00 +9988.52+7.18*T+0.071429*GBCCCA# +0.928571*GHSERMG#; 6000.00 N REF:13 ! PARAMETER G(CAZN13,SR:MG;0) 273.00 +0.071429*GHSERSR# +0.928571*GHSERMG#; 6000.00 N REF:2 ! PARAMETER G(CAZN13,SR:ZN;0) 273.00 -19005+6.6984*T+0.071429*GHSERSR# +0.928571*GHSERZN#; 6000.00 N REF:2 ! $ $*************************************************************************** $ interaction parameters $*************************************************************************** PARAMETER L(CAZN13,CA:MG,ZN;0) 273.00 -36000+2.25*T; 6000.00 N REF:pov14 ! PARAMETER L(CAZN13,CA:MG,ZN;1) 273.00 -3737.32; 6000.00 N REF:13 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: CA3ZN $########################################################################### $ PHASE CA3ZN % 2 3 1 > >> 1 ! CONSTITUENT CA3ZN :CA : ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(CA3ZN,CA:ZN;0) 273.00 -38500+1.75*T+3*GHSERCA# +GHSERZN#; 6000.00 N REF:pov14 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: CA5ZN3 $########################################################################### $ PHASE CA5ZN3 % 2 0.625 0.375 > >> 1 ! CONSTITUENT CA5ZN3 :CA : ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(CA5ZN3,CA:ZN;0) 273.00 -14486.92+0.88*T+0.625*GHSERCA# +0.375*GHSERZN#; 6000.00 N REF:pov14 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: IM1 $########################################################################### $ PHASE IM1 % 3 0.166667 0.166667 0.66667 > >> 3 ! CONSTITUENT IM1 :CA : MG,ZN% : MG%,ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(IM1,CA:ZN:MG;0) 273.00 -20200+20*T+0.166667*GBCCCA# +0.166667*GHSERZN#+0.666667*GHSERMG#; 6000.00 N REF:pov14 ! PARAMETER G(IM1,CA:ZN:ZN;0) 273.00 -3500+1*T+0.166667*GBCCCA# +0.166667*GHSERZN#+0.666667*GHSERZN#; 6000.00 N REF:pov14 ! PARAMETER G(IM1,CA:MG:MG;0) 273.00 -3500+1*T+0.166667*GBCCCA# +0.166667*GHSERMG#+0.666667*GHSERMG#; 6000.00 N REF:pov14 ! PARAMETER G(IM1,CA:MG:ZN;0) 273.00 -20200+7.5*T+0.166667*GBCCCA# +0.166667*GHSERMG#+0.666667*GHSERZN#; 6000.00 N REF:pov14 ! $ $*************************************************************************** $ interaction parameters $*************************************************************************** PARAMETER L(IM1,CA:ZN,MG:ZN;0) 273.00 -28500; 6000.00 N REF:pov14 ! PARAMETER L(IM1,CA:ZN,MG:ZN;1) 273.00 -2000; 6000.00 N REF:pov14 ! PARAMETER L(IM1,CA:ZN:MG,ZN;0) 273.00 -9000; 6000.00 N REF:pov14 ! PARAMETER L(IM1,CA:ZN:MG,ZN;1) 273.00 -10000; 6000.00 N REF:pov14 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: IM2 $########################################################################### $ PHASE IM2 % 3 0.14 0.16 0.7 > >> 1 ! CONSTITUENT IM2 :CA : MG : ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(IM2,CA:MG:ZN;0) 273.00 -23000+7.5*T+0.14*GBCCCA# +0.16*GHSERMG#+0.7*GHSERZN#; 6000.00 N REF:pov14 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: IM3 $########################################################################### $ PHASE IM3 % 3 0.065217 0.282609 0.652174 > >> 2 ! CONSTITUENT IM3 :CA : CA,MG% : MG,ZN% : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(IM3,CA:CA:MG;0) 273.00 +4549.78+0.065217*GBCCCA# +0.282609*GBCCCA#+0.652174*GHSERMG#; 6000.00 N REF:13 ! PARAMETER G(IM3,CA:CA:ZN;0) 273.00 +3184.85+0.065217*GBCCCA# +0.282609*GBCCCA#+0.652174*GHSERZN#; 6000.00 N REF:13 ! PARAMETER G(IM3,CA:MG:MG;0) 273.00 +5459.74+0.065217*GBCCCA# +0.282609*GHSERMG#+0.652174*GHSERMG#; 6000.00 N REF:13 ! PARAMETER G(IM3,CA:MG:ZN;0) 273.00 -27000+22*T+0.065217*GBCCCA# +0.282609*GHSERMG#+0.652174*GHSERZN#; 6000.00 N REF:pov14 ! $ $*************************************************************************** $ interaction parameters $*************************************************************************** PARAMETER L(IM3,CA:CA,MG:ZN;0) 273.00 -39000; 6000.00 N REF:pov14 ! PARAMETER L(IM3,CA:MG:MG,ZN;0) 273.00 -2700; 6000.00 N REF:pov14 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: IM4 $########################################################################### $ PHASE IM4 % 3 0.02 0.55 0.43 > >> 1 ! CONSTITUENT IM4 :CA : MG : ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(IM4,CA:MG:ZN;0) 273.00 -11250+4.5*T+0.02*GBCCCA# +0.55*GHSERMG#+0.43*GHSERZN#; 6000.00 N REF:pov14 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: LAV_C14 $########################################################################### $ PHASE LAV_C14 % 2 .66667 .33333 > Hexagonal close-packed. >> 3 ! CONSTITUENT LAV_C14 :AL,CA,MG%,SR,ZN : AL,CA%,MG,SR,ZN% : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(LAV_C14,AL:AL;0) 273.00 +5000+GHSERAL#; 6000.00 N REF:2 ! PARAMETER G(LAV_C14,CA:AL;0) 273.00 +15000 +0.33333*GHSERAL#+0.66667*GHSERCA#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C14,MG:AL;0) 273.00 +5776.333-5.6*T +0.33333*GHSERAL#+0.66667*GHSERMG#; 6000.00 N REF:2 ! PARAMETER G(LAV_C14,SR:AL;0) 273.00 +15000 +0.33333*GHSERAL#+0.66667*GHSERSR#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C14,ZN:AL;0) 273.00 +5000+0.66667*GHSERZN# +0.33333*GHSERAL#; 6000.00 N REF:2 ! PARAMETER G(LAV_C14,AL:CA;0) 273.00 +0.66667*GHSERAL# +0.3333*GHSERCA#-24700+3*T; 6000.00 N REF:14 ! PARAMETER G(LAV_C14,CA:CA;0) 273.00 +GBCCCA#+42078.60; 6000.00 N REF:13 ! PARAMETER G(LAV_C14,MG:CA;0) 273.00 +0.66667*GHSERMG# +0.3333*GBCCCA#-13750+4.85*T; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C14,SR:CA;0) 273.00 +0.66667*GHSERSR# +0.3333*GBCCCA#+15000; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C14,ZN:CA;0) 273.00 -15325.61 +0.33333*GBCCCA#+0.66667*GHSERZN#; 6000.00 N REF:13 ! PARAMETER G(LAV_C14,AL:MG;0) 273.00 +4223.7+5.6*T +0.33333*GHSERMG#+0.66667*GHSERAL#; 6000.00 N REF:2 ! PARAMETER G(LAV_C14,CA:MG;0) 273.00 +0.33333*GHSERMG# +0.66667*GBCCCA#+5573.30; 6000.00 N REF:13 ! PARAMETER G(LAV_C14,MG:MG;0) 273.00 +3884.6+GHSERMG#; 6000.00 N REF:13 ! PARAMETER G(LAV_C14,SR:MG;0) 273.00 +10000+0.66667*GHSERSR# +0.33333*GHSERMG#+7330.596+0.378293833*T; 3.00000E+03 N REF:2 ! PARAMETER G(LAV_C14,ZN:MG;0) 273.00 -11000+1.5*T +0.33333*GHSERMG#+0.66667*GHSERZN#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C14,AL:SR;0) 273.00 +0.66667*GHSERAL# +0.33333*GHSERSR#+15000; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C14,CA:SR;0) 273.00 +0.66667*GHSERCA# +0.33333*GHSERSR#+15000; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C14,MG:SR;0) 273.00 +0.66667*GHSERMG# +0.33333*GHSERSR#-7330.596-0.378293833*T; 6000.00 N REF:2 ! PARAMETER G(LAV_C14,SR:SR;0) 273.00 +5000+GHSERSR#; 6000.00 N REF:2 ! PARAMETER G(LAV_C14,ZN:SR;0) 273.00 +0.66667*GHSERZN# +0.33333*GHSERSR#+15000; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C14,AL:ZN;0) 273.00 +5000+0.66667*GHSERAL# +0.33333*GHSERZN#; 6000.00 N REF:2 ! PARAMETER G(LAV_C14,CA:ZN;0) 273.00 +19533.73+0.33333*GHSERZN# +0.66667*GBCCCA#; 6000.00 N REF:13 ! PARAMETER G(LAV_C14,MG:ZN;0) 273.00 +21789.88 +0.33333*GHSERZN#+0.66667*GHSERMG#; 6000.00 N REF:13 ! PARAMETER G(LAV_C14,SR:ZN;0) 273.00 +15000 +0.33333*GHSERZN#+0.66667*GHSERSR#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C14,ZN:ZN;0) 273.00 +7507.30+GHSERZN#; 6000.00 N REF:13 ! $ $*************************************************************************** $ interaction parameters $*************************************************************************** PARAMETER L(LAV_C14,AL:AL,MG;0) 273.00 +2666.7; 6000.00 N REF:2 ! PARAMETER L(LAV_C14,AL:AL,ZN;0) 273.00 -2500-6*T; 6000.00 N REF:2 ! PARAMETER L(LAV_C14,AL,MG:AL;0) 273.00 +5000; 6000.00 N REF:2 ! PARAMETER L(LAV_C14,AL,MG:MG;0) 273.00 +5000; 6000.00 N REF:2 ! PARAMETER L(LAV_C14,AL,MG:CA;0) 273.00 -2000; 6000.00 N REF:pov14 ! PARAMETER L(LAV_C14,AL:MG,ZN;0) 273.00 +2666.7; 6000.00 N REF:2 ! PARAMETER L(LAV_C14,AL,MG:ZN;0) 273.00 +2666.7; 6000.00 N REF:2 ! PARAMETER L(LAV_C14,AL,ZN:MG;0) 273.00 -2500-6*T; 6000.00 N REF:2 ! PARAMETER L(LAV_C14,CA:CA,MG;0) 273.00 +14006; 6000.00 N REF:13 ! PARAMETER G(LAV_C14,CA:CA,ZN;0) 273.00 +1e-8; 6000.00 N REF:13 ! PARAMETER L(LAV_C14,CA:MG,ZN;0) 273.00 +1e-8; 6000.00 N REF:13 ! PARAMETER L(LAV_C14,CA,MG:CA;0) 273.00 +14006; 6000.00 N REF:13 ! PARAMETER L(LAV_C14,CA,MG:MG;0) 273.00 +14006; 6000.00 N REF:13 ! PARAMETER L(LAV_C14,CA,MG:ZN;0) 273.00 +1e-8; 6000.00 N REF:13 ! PARAMETER L(LAV_C14,CA,ZN:CA;0) 273.00 +1e-8; 6000.00 N REF:13 ! PARAMETER L(LAV_C14,CA,ZN:MG;0) 273.00 +1e-8; 6000.00 N REF:13 ! PARAMETER L(LAV_C14,CA,ZN:ZN;0) 273.00 +1e-8; 6000.00 N REF:13 ! PARAMETER L(LAV_C14,MG:AL,MG;0) 273.00 +2666.7; 6000.00 N REF:2 ! PARAMETER L(LAV_C14,MG:CA,MG;0) 273.00 +14006; 6000.00 N REF:13 ! PARAMETER L(LAV_C14,MG:CA,ZN;0) 273.00 -32000; 6000.00 N REF:pov14 ! PARAMETER L(LAV_C14,MG:CA,ZN;1) 273.00 +1e-8; 6000.00 N REF:pov14 ! PARAMETER L(LAV_C14,MG:CA,ZN;2) 273.00 +1e-8; 6000.00 N REF:pov14 ! PARAMETER L(LAV_C14,MG:MG,SR;0) 273.00 +13333.3; 6000.00 N REF:2 ! PARAMETER L(LAV_C14,MG:MG,ZN;0) 273.00 1.4; 6000.00 N REF:13 ! PARAMETER L(LAV_C14,MG,SR:MG;0) 273.00 +1e-8; 6000.00 N REF:2 ! PARAMETER L(LAV_C14,MG,SR:SR;0) 273.00 +30000; 6000.00 N REF:2 ! PARAMETER L(LAV_C14,MG,ZN:AL;0) 273.00 +11666.7; 6000.00 N REF:2 ! PARAMETER L(LAV_C14,MG,ZN:CA;0) 273.00 +1e-8; 6000.00 N REF:13 ! PARAMETER L(LAV_C14,MG,ZN:MG;0) 273.00 +11288; 6000.00 N REF:13 ! PARAMETER L(LAV_C14,MG,ZN:ZN;0) 273.00 +11288; 6000.00 N REF:13 ! PARAMETER L(LAV_C14,SR:MG,SR;0) 273.00 +1e-8; 6000.00 N REF:2 ! PARAMETER L(LAV_C14,ZN:AL,MG;0) 273.00 +5000; 6000.00 N REF:2 ! PARAMETER L(LAV_C14,ZN:AL,ZN;0) 273.00 -2500-6*T; 6000.00 N REF:2 ! PARAMETER L(LAV_C14,ZN:CA,MG;0) 273.00 +1e-8; 6000.00 N REF:13 ! PARAMETER L(LAV_C14,ZN:MG,ZN;0) 273.00 1.4; 6000.00 N REF:13 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: LAV_C15 $########################################################################### $ PHASE LAV_C15 % 2 .66667 .33333 > Cubic, space group Fd3-m. >> 3 ! CONSTITUENT LAV_C15 :AL%,CA,MG,SI,ZN : AL,CA,MG%,SI,ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(LAV_C15,AL:AL;0) 273.00 +15391+6.528*T+GHSERAL#; 6000.00 N REF:2 ! PARAMETER G(LAV_C15,CA:AL;0) 273.00 +46508+6.528*T +0.66667*GHSERCA#+0.33333*GHSERAL#; 6000.00 N REF:2 ! PARAMETER G(LAV_C15,MG:AL;0) 273.00 +34990.32-5.48816*T +0.66667*GHSERMG#+0.33333*GHSERAL#; 6000.00 N REF:2 ! PARAMETER G(LAV_C15,SI:AL;0) 273.00 +15000 +0.66667*GHSERSI#+0.33333*GHSERAL#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C15,ZN:AL;0) 273.00 +15000 +0.66667*GHSERZN#+0.33333*GHSERAL#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C15,AL:CA;0) 273.00 -32047.667+6.528*T +0.66667*GHSERAL#+0.33333*GHSERCA#; 6000.00 N REF:2 ! PARAMETER G(LAV_C15,CA:CA;0) 273.00 +8201+6.528*T+GHSERCA#; 6000.00 N REF:2 ! PARAMETER G(LAV_C15,MG:CA;0) 273.00 -4820 +0.66667*GHSERMG#+0.33333*GHSERCA#; 6000.00 N REF:14 ! PARAMETER G(LAV_C15,SI:CA;0) 273.00 +15000 +0.66667*GHSERSI#+0.33333*GHSERCA#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C15,ZN:CA;0) 273.00 +15000 +0.66667*GHSERZN#+0.33333*GHSERCA#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C15,AL:MG;0) 273.00 +10000+1.333*T +0.66667*GHSERAL#+0.33333*GHSERMG#; 6000.00 N REF:2 ! PARAMETER G(LAV_C15,CA:MG;0) 273.00 +15000 +0.66667*GHSERCA#+0.33333*GHSERMG; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C15,MG:MG;0) 273.00 +5000+GHSERMG#; 6000.00 N REF:2 ! PARAMETER G(LAV_C15,SI:MG;0) 273.00 +13679.67+2.08333*T +0.66667*GHSERSI#+0.33333*GHSERMG#; 6000.00 N REF:3 ! PARAMETER G(LAV_C15,ZN:MG;0) 273.00 -8451.817+2.9463*T +0.66667*GHSERZN#+0.33333*GHSERMG#; 6000.00 N REF:2 ! PARAMETER G(LAV_C15,AL:SI;0) 273.00 +15000+0.66667*GHSERAL# +0.33333*GHSERSI#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C15,CA:SI;0) 273.00 +15000+0.66667*GHSERCA# +0.33333*GHSERSI#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C15,MG:SI;0) 273.00 +34990.32-5.48816*T +0.66667*GHSERMG#+0.33333*GHSERSI#; 6000.00 N REF:3 ! PARAMETER G(LAV_C15,SI:SI;0) 273.00 +5000.0+GHSERSI#; 6000.00 N REF:3 ! PARAMETER G(LAV_C15,ZN:SI;0) 273.00 +15000+0.66667*GHSERZN# +0.33333*GHSERSI#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C15,AL:ZN;0) 273.00 +15000 +0.66667*GHSERAL#+0.33333*GHSERZN#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C15,CA:ZN;0) 273.00 +15000 +0.66667*GHSERCA#+0.33333*GHSERZN#; 6000.00 N REF:2 ! PARAMETER G(LAV_C15,MG:ZN;0) 273.00 +18454.763-2.9463*T +0.66667*GHSERMG#+0.33333*GHSERZN#; 6000.00 N REF:2 ! PARAMETER G(LAV_C15,SI:ZN;0) 273.00 +15000 +0.66667*GHSERSI#+0.33333*GHSERZN#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C15,ZN:ZN;0) 273.00 +5000+GHSERZN#; 6000.00 N REF:2 ! $ $*************************************************************************** $ interaction parameters $*************************************************************************** PARAMETER L(LAV_C15,AL:AL,MG;0) 273.00 +2666.7; 6000.00 N REF:2 ! PARAMETER L(LAV_C15,AL,MG:AL;0) 273.00 +5000; 6000.00 N REF:2 ! PARAMETER L(LAV_C15,AL,MG:MG;0) 273.00 +5000; 6000.00 N REF:2 ! PARAMETER L(LAV_C15,MG:AL,MG;0) 273.00 +2666.7; 6000.00 N REF:2 ! PARAMETER L(LAV_C15,MG:MG,SI;0) 273.00 +2666.667; 6000.00 N REF:3 ! PARAMETER L(LAV_C15,MG:MG,ZN;0) 273.00 +2666.7; 6000.00 N REF:2 ! PARAMETER L(LAV_C15,MG,SI:MG;0) 273.00 +5000; 6000.00 N REF:3 ! PARAMETER L(LAV_C15,MG,ZN:MG;0) 273.00 +11666.7; 6000.00 N REF:2 ! PARAMETER L(LAV_C15,MG,ZN:ZN;0) 273.00 +11666.7; 6000.00 N REF:2 ! PARAMETER L(LAV_C15,SI:SI,MG;0) 273.00 +2666.667; 6000.00 N REF:3 ! PARAMETER L(LAV_C15,SI,MG:SI;0) 273.00 +5000; 6000.00 N REF:3 ! PARAMETER L(LAV_C15,ZN:MG,ZN;0) 273.00 +2666.7; 6000.00 N REF:2 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: LAV_C36 $########################################################################### $ PHASE LAV_C36 % 3 .48 .187 0.333 > Hexagonal close-packed. >> 3 ! CONSTITUENT LAV_C36 :AL,ZN : AL,MG%,ZN : CA%,MG : ! PARAMETER G(LAV_C36,AL:MG:CA;0) 273.00 -23500+0.48*GHSERAL# +0.187*GHSERMG#+0.333*GHSERCA#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C36,AL:MG:MG;0) 273.00 -400+0.5*T +0.48*GHSERAL#+0.187*GHSERMG#+0.333*GHSERMG#; 6000.00 N REF:14 ! PARAMETER G(LAV_C36,AL:AL:MG;0) 273.00 +2350+2*T +0.48*GHSERAL#+0.187*GHSERAL#+0.333*GHSERMG#; 6000.00 N REF:14 ! PARAMETER G(LAV_C36,AL:AL:CA;0) 273.00 -27900+5*T +0.48*GHSERAL#+0.187*GHSERAL#+0.333*GHSERCA#; 6000.00 N REF:14 ! PARAMETER G(LAV_C36,AL:ZN:CA;0) 273.00 +15000+0.48*GHSERAL# +0.187*GHSERZN#+0.333*GHSERCA#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C36,AL:ZN:MG;0) 273.00 +0.48*GHSERAL# +0.187*GHSERZN#+0.333*GHSERMG#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C36,ZN:AL:CA;0) 273.00 +15000 +0.48*GHSERZN#+0.187*GHSERAL#+0.333*GHSERCA#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C36,ZN:AL:MG;0) 273.00 +0.48*GHSERZN# +0.187*GHSERAL#+0.333*GHSERMG#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C36,ZN:MG:CA;0) 273.00 +15000 +0.48*GHSERZN#+0.187*GHSERMG#+0.333*GHSERCA#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C36,ZN:MG:MG;0) 273.00 -5000 +0.48*GHSERZN#+0.187*GHSERMG#+0.333*GHSERMG#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C36,ZN:ZN:CA;0) 273.00 +15000 +0.48*GHSERZN#+0.187*GHSERZN#+0.333*GHSERCA#; 6000.00 N REF:pov14 ! PARAMETER G(LAV_C36,ZN:ZN:MG;0) 273.00 -11118.483+2.9463*T +0.48*GHSERZN#+0.187*GHSERZN#+0.333*GHSERMG#; 6000.00 N REF:pov14 ! PARAMETER L(LAV_C36,AL:AL:CA,MG;0) 273.00 -4700; 6000.00 N REF:14 ! PARAMETER L(LAV_C36,AL:MG:CA,MG;0) 273.00 -4700; 6000.00 N REF:14 ! PARAMETER L(LAV_C36,AL:AL,MG:CA;0) 273.00 -1000; 6000.00 N REF:14 ! PARAMETER L(LAV_C36,AL:AL,MG:MG;0) 273.00 -4550; 6000.00 N REF:14 ! $ $########################################################################### $ THERMODYNAMIC DATA: MG2SI $########################################################################### $ PHASE MG2SI % 2 2 1 > Face-centered cubic. >> 2 ! CONSTITUENT MG2SI :MG : SI : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(MG2SI,MG:SI;0) 273.00 -92250.0+440.4*T-75.9*T*LN(T) -0.0018*T**2+630000*T**(-1); 6000.00 N REF:3 ! $ $########################################################################### $ THERMODYNAMIC DATA: MG17SR2 $########################################################################### $ PHASE MG17X2 % 2 17 2 > >> 1 ! CONSTITUENT MG17X2 :MG : SR : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(MG17X2,MG:SR;0) 273.00 -43983.66-24.846882*T +17*GHSERMG#+2*GHSERSR#; 6000.00 N REF:2 ! $ $########################################################################### $ THERMODYNAMIC DATA: MG23X6 $########################################################################### $ PHASE MG23X6 % 2 23 6 > >> 1 ! CONSTITUENT MG23X6 :MG : SR : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(MG23X6,MG:SR;0) 273.00 -135297.56-28.46587*T +23*GHSERMG#+6*GHSERSR#; 6000.00 N REF:2 ! $ $########################################################################### $ THERMODYNAMIC DATA: MG38SR9 $########################################################################### $ PHASE MG38SR9 % 2 38 9 > >> 1 ! CONSTITUENT MG38SR9 :MG : SR : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(MG38SR9,MG:SR;0) 273.00 -204182.2-47.880167*T +38*GHSERMG#+9*GHSERSR#; 6000.00 N REF:2 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: MGZN $########################################################################### $ PHASE MGZN % 2 .48 .52 > >> 2 ! CONSTITUENT MGZN :MG : AL,ZN% : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(MGZN,MG:AL;0) 273.00 -400+0.1*T+0.48*GHSERMG# +0.52*GHSERAL#; 6000.00 N REF:2 ! PARAMETER G(MGZN,MG:ZN;0) 273.00 -10000+2.75*T +0.48*GHSERMG#+0.52*GHSERZN#; 6000.00 N REF:pov14 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: MG2ZN11 $########################################################################### $ PHASE MG2ZN11 % 2 .153846 .846154 > Cubic, space group PM3-. >> 2 ! CONSTITUENT MG2ZN11 :MG : AL,SI,ZN% : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(MG2ZN11,MG:AL;0) 273.00 +10000-2*T+0.153846*GHSERMG# +0.846154*GHSERAL#; 6000.00 N REF:2 ! PARAMETER G(MG2ZN11,MG:SI;0) 273.00 +619491.5+1.42*T +0.153846*GHSERMG#+0.846154*GHSERSI#; 6000.00 N REF:11 ! PARAMETER G(MG2ZN11,MG:ZN;0) 273.00 -7500+3.75*T +0.153846*GHSERMG#+0.846154*GHSERZN#; 6000.00 N REF:pov14 ! $ $*************************************************************************** $ interaction parameters $*************************************************************************** PARAMETER L(MG2ZN11,MG:SI,ZN;0) 273.00 -118047.9+91.62*T; 6000.00 N REF:11 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: MG2ZN3 $########################################################################### $ PHASE MG2ZN3 % 2 .4 .6 > Monoclinic, space group B2/m. >> 2 ! CONSTITUENT MG2ZN3 :MG : AL,ZN% : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(MG2ZN3,MG:AL;0) 273.00 +200-0.04*T+0.4*GHSERMG# +0.6*GHSERAL#; 6000.00 N REF:2 ! PARAMETER G(MG2ZN3,MG:ZN;0) 273.00 -11000+2.5*T+0.4*GHSERMG# +0.6*GHSERZN#; 6000.00 N REF:pov14 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: MG7ZN3 $########################################################################### $ PHASE MG7ZN3 % 2 .71831 .28169 > Orthorhombic, space group Immm. >> 2 ! CONSTITUENT MG7ZN3 :MG : ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(MG7ZN3,MG:ZN;0) 273.00 -5000+0.7*T+0.71831*GHSERMG# +0.28169*GHSERZN#; 6000.00 N REF:pov14 ! $########################################################################### $ THERMODYNAMIC DATA: MN3SI $########################################################################### $ PHASE MN3SI % 2 3 1 > fcc Fe3Al-type >> 2 ! CONSTITUENT MN3SI :MN : SI : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(MN3SI,MN:SI;0) 273.00 -124189.87+782.4373*T-131.682*T*LN(T) -7.770061E-03*T**2+1.6572E+06*T**(-1); 950.00 Y -1.197406E+05+777.7538*T-131.6820*T*LN(T) -7.770061E-03*T**2+1.6572E+06*T**(-1); 6000.00 N REF:3 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: PHI $########################################################################### $ PHASE PHI % 2 6 5 > Orthorhombic [REF:C1] >> 2 ! CONSTITUENT PHI :MG : AL,ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(PHI,MG:AL;0) 273.00 -15400-16.5*T+5*GHSERAL# +6*GHSERMG#; 6000.00 N REF:2 ! PARAMETER G(PHI,MG:ZN;0) 273.00 -79530+20.9*T+6*GHSERMG# +5*GHSERZN#; 6000.00 N REF:2 ! $ $*************************************************************************** $ interaction parameters $*************************************************************************** PARAMETER L(PHI,MG:AL,ZN;0) 273.00 -23100+11*T; 6000.00 N REF:2 ! $ $########################################################################### $ THERMODYNAMIC DATA: SI_DIAMOND_A4 $########################################################################### $ PHASE SI_DIAMOND_A4 % 1 1 > Space group Fd3m, prototype: C(diamond) >> 1 ! CONSTITUENT SI_DIAMOND_A4 :AL,SI%,ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(SI_DIAMOND_A4,AL;0) 273.00 +10000+15*T+GHSERAL#; 6000.00 N REF:pov14 ! PARAMETER G(SI_DIAMOND_A4,SI;0) 273.00 +GHSERSI#; 6000.00 N REF:3 ! PARAMETER G(SI_DIAMOND_A4,ZN;0) 273.00 +30*T+GHSERZN#; 6000.00 N REF:3 ! $ $*************************************************************************** $ interaction parameters $*************************************************************************** PARAMETER L(SI_DIAMOND_A4,AL,SI;0) 273.00 +113246.16-47.55509*T; 6000.00 N REF:3 ! PARAMETER L(SI_DIAMOND_A4,SI,ZN;0) 273.00 +100*T; 6000.00 N REF:3 ! $ $########################################################################### $ THERMODYNAMIC DATA: SRZN $########################################################################### $ PHASE SRZN % 2 1 1 > >> 1 ! CONSTITUENT SRZN :SR : ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(SRZN,SR:ZN;0) 273.00 -38226+12.55*T+GHSERSR# +GHSERZN#; 6000.00 N REF:2 ! $ $########################################################################### $ THERMODYNAMIC DATA: SRZN5_LT $########################################################################### $ PHASE SRZN5_LT % 2 1 5 > >> 1 ! CONSTITUENT SRZN5_LT :SR : ZN : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(SRZN5_LT,SR:ZN;0) 273.00 -122011+31.403*T+GHSERSR# +5*GHSERZN#; 6000.00 N REF:2 ! $ $########################################################################### $ THERMODYNAMIC PARAMETERS: TAU $########################################################################### $ PHASE TAU % 4 26 6 48 1 > Cubic. [REF:C5] >> 2 ! CONSTITUENT TAU :MG : AL,MG% : AL%,MG,ZN% : AL : ! $ $*************************************************************************** $ end-member parameters $*************************************************************************** PARAMETER G(TAU,MG:AL:AL:AL;0) 273.00 -105.3*T+55*GHSERAL# +26*GHSERMG#; 6000.00 N REF:2 ! PARAMETER G(TAU,MG:MG:AL:AL;0) 273.00 -81000-186.3*T+49*GHSERAL# +32*GHSERMG#; 6000.00 N REF:2 ! PARAMETER G(TAU,MG:AL:MG:AL;0) 273.00 +1053000+405*T+7*GHSERAL# +74*GHSERMG#; 6000.00 N REF:2 ! PARAMETER G(TAU,MG:MG:MG:AL;0) 273.00 +405000+243*T+GHSERAL# +80*GHSERMG#; 6000.00 N REF:2 ! PARAMETER G(TAU,MG:AL:ZN:AL;0) 273.00 -832680+162*T+7*GHSERAL# +26*GHSERMG#+48*GHSERZN#; 6000.00 N REF:2 ! PARAMETER G(TAU,MG:MG:ZN:AL;0) 273.00 -811620+162*T+GHSERAL# +32*GHSERMG#+48*GHSERZN#; 6000.00 N REF:2 ! $ $*************************************************************************** $ interaction parameters $*************************************************************************** PARAMETER L(TAU,MG:AL:AL,MG:AL;0) 273.00 -202500-40.5*T; 6000.00 N REF:2 ! PARAMETER L(TAU,MG:AL:AL,ZN:AL;0) 273.00 -16200+243*T; 6000.00 N REF:2 ! PARAMETER L(TAU,MG:MG:AL,MG:AL;0) 273.00 -202500-40.5*T; 6000.00 N REF:2 ! PARAMETER L(TAU,MG:MG:AL,ZN:AL;0) 273.00 -105300+243*T; 6000.00 N REF:2 ! PARAMETER L(TAU,MG:AL:MG,ZN:AL;0) 273.00 +243000+81*T; 6000.00 N REF:2 ! PARAMETER L(TAU,MG:MG:MG,ZN:AL;0) 273.00 +243000+81*T; 6000.00 N REF:2 ! $ $*************************************************************************** $ $ E) References $ $*************************************************************************** $ A00201-0 unary A.T. Dinsdale, SGTE Data of pure elements, CALPHAD, Vol. 15, No. 4, pp. 317-425, 1991. A00187-1 Al-Mg-Mn Y. Du, J. Wang, J. Zhao, J.C. Schuster et al., Reassessment of the Al-Mn system and a thermodynamic description of the Al-Mg-Mn system, Int. J. Mater. Res. Vol. 98, No. 9, pp. 855-871, 2007. A00260-2 Mg-Al-Zn-Ca-Sr Yu Zhong, Investigation in Mg-Al-Ca-Sr-Zn system by computational thermodynamics approach coupled with first-principles energetics and experiments, Thesis, Pennsylvania State University, 2005. A00316-3 bin, tern N. Saunders, COST 507: Thermochemical database for light metal alloys, Vol. 2, pp 23-27, 1998. 149, 1992. A00040-4 Al-C-Cr-Cu-Fe-Mo-... J. Miettinen, Thermodynamic substitutional solution data for steels, Report TKK-MK-76, pp 1-24, 1999. A00030-5 Mn-based J. Miettinen, Thermodynamic solution phase data for binary Mn-based systems, CALPHAD, Vol. 25, No. 1, pp 43-58, 2001. A00166-6 Al-Mg-Si J. Lacaze and R. Valdes, CALPHAD-type assessment of the Al-Mg-Si system, Monatshefte f. Chemie, Vol. 136, pp. 1899-1907, 2005. A00211-7 Al-Mn-Si Y. Du, J.C. Schuster,F. Weitzer, N. Krendelsberger, B. Huang et al., A thermodynamic description of the Al-Mn-Si system over the entire composition and temperature range, Metall. Mater. Trans. A, Vol. 35A, pp. 1613-1628, 2004. A00172-8 Mg-Si-Li D. Kevorkov, R. Schmid-Fetzer, F. Zhang, Phase equilibria and thermodynamics of the Mg-Si-Li system and remodeling of the Mg-Si system, J. Phase Equilib. Diffusion, Vol. 25, pp. 140-151, 2004. A00206-9 Al-Cu-Si C.-Y. He, J. Du et al., Experimental investigation and thermodynamic modeling of the Al-Cu-Si system, CALPHAD, Vol. 33, pp. 200-210, 2009. A00297-11 Mg-Si-Zn M. Wang, P. Wang, S. Liu, Y. Du, H. Xu, W. Zhang, Experimental investigation and thermodynamic modeling of the Mg-Si-Zn system, CALPHAD, Vol. 35, pp. 183-190, 2011. A00323-12 Mg-Ca-Zn C.O. Brubaker, Z.-K. Liu, A computational thermodynamic model of the Ca-Mg-Zn system, J. Alloys Cmpd., Vol. 370, pp. 114-122, 2004. A00324-13 Mg-Ca-Zn M. Mezbahul-Islam, Y.N. Zhang, C. Shekhar, M. Medraj, Critical assessment and thermodynamic modeling of Mg-Ca-Zn supported by key experiments, CALPHAD, 2014, in press. A00330-14 Al-Ca-Mg A. Janz, J. Gröbner, H. Cao, J. Zhu, Y.A. Chang, R. Schmid-Fetzer, Thermodynamic modeling of the Mg-Al-Ca system, Acta Mater., Vol. 57, pp. 682-694, 2009. A00332-16 Mn-Zn J. Miettinen, Thermodynamic description of the Cu-Mn-Zn system in the copper-rich corner, CALPHAD, Vol. 28, pp. 313-320, 2004. A00333-17 Mg-Zn P. Ghosh, M. Medraj, Thermodynamic calculation of the Mg-Mn-Zn and Mg-Mn-Ce systems and re-optimisation of their constitutive binaries, CALPHAD, Vol. 41, pp. 89-107, 2013. pov11 E. Povoden-Karadeniz, unpublished 2011. pov13 E. Povoden-Karadeniz, unpublished 2013. pov14 E. Povoden-Karadeniz, unpublished 2014. pov15 E. Povoden-Karadeniz, unpublished 2015. $########################################################################### $########################################################################### $########################################################################### $ Commentary sources C00030-1 PHI-Phase P. Donnadieu, A. Quivy, T. Tarfa, P. Ochin, A. Dezellus et al., On the crystal structure and solubility range of the ternary phi phase in the Mg-Al-Zn system, Z. Metallkd., Vol. 88, pp. 911-916, 1997. C00031-2 Al-Mg-Mn-Zn M. Ohno, D. Mirkovic, R. Schmid-Fetzer, Liquidus and solidus temperatures of Mg-rich Mg-Al-Mn-Zn alloys, Acta Mater., Vol. 54, pp. 3883-3891, 1996. C00032-3 AZ61 E. Dhuka, N. Lohja, H. Oettel, D. Heger, Precipitation in Mg alloy AZ61 in dependence of various heat treatments processes, Association of metallurgical engineers Serbia and Montenegro. C00033-4 AZ-alloy Z.-Z. Shi, W-Z. Zhang, Interpretation of crystallographic morphologies of precipitates in Mg alloys with a secondary CCSL model, Mater. Sci. Forum, Vol. 686, pp. 192-196, 2011. C00034-5 Al-Mg-Zn prec. N. Afify, A.-F. Gaber, G. Abbady, Fine scale precipitates in Al-Mg-Zn alloys after various aging temperatures, Mater. Sc. Appl., Vol. 2, pp. 427-434, 2011. C00035-6 AZ91, precipitates K.N. Braszczynska-Malik, in: Magnesium alloys - Design, processing and properties, chapter 5, Precipitates of gamma-Mg17Al12 phase in AZ91 alloy, pp. 95-112. C00036-7 AZ31-series, precip. R. Gonzalez-Martinez, J. Göken, D. Letzig, K. Steinhoff, K.U. Kainer, Influence of aging on damping of the magnesium-aluminium-zinc series, J. Alloys Compd., Vol. 437, pp. 127-132, 2007.